Wet high-energy milling and uniaxial pressing are used to fabricate CaO-stabilized tetragonal zirconia polycrystalline ceramic (Ca-TZP) with decent mechanical characteristics, i.e., a hardness of 11.5 GPa, Young's modulus of 230 GPa, and fracture toughness of 13 MPa·m0.5. The effect of CaO concentration and the sintering temperature on phase composition and mechanical characteristics of CaO-stabilized zirconia ceramic made of baddeleyite is investigated.
Keywords: baddeleyite; high-energy milling; mechanical characteristics; phase composition; zirconia ceramic.