A thin film of unsubstituted polythiophene (PT), an insoluble conjugated polymer, with molecular chains uniaxially oriented in plane was prepared by the friction transfer method. The structure of highly oriented thin films of PT was investigated using grazing-incidence X-ray diffraction (GIXD), ultraviolet-visible (UV-vis) spectroscopy, and infrared (IR) spectroscopy. The polarized UV-vis and IR spectra and GIXD measurements showed the PT molecular chains were well aligned in parallel to the friction direction. The GIXD studies clarified that the polymer backbones were aligned with very narrow distribution, such that the half-width was about 4 degrees. The degree of orientation of the PT friction-transferred film was higher compared with those of regioregular poly(3-alkylthiophene)s. Moreover, the GIXD results show a preferred orientation where the a-axis is perpendicular to the substrate plane.
Keywords: X-ray diffraction; conjugated polymers; molecular orientation; oriented films; polythiophene.