Hyaluronic acid (HA) of different molar masses (respectively 38,000, 140,000 and 1,200,000 g.mol-1) have been functionalized with a commercial poly(etheramine), Jeffamine® M2005, in order to devise physical thermo-responsive hydrogels. Two routes have been studied, involving the use of either water for the first one or of N,N'-Dimethylformamide (DMF), a polar aprotic solvent, for the second one. In the case of the water route, the reaction was performed using a mixture of N-(3-Dimethylaminopropyl)-N'-ethylcarbodiimide (EDC) and N-hydroxysuccinimide (NHS) as coupling reagents. The reaction was optimized while making sure no free M2005 remained in the final material, leading to M2005 grafting degrees of about 4%, which enabled the formation of hydrogels by increasing the temperature. In the case of the organic solvent route, propylphosphonic anhydride T3P® was used as a coupling reagent in DMF, resulting in a M2005 grafting degree of around 8% with better thermo-responsive properties of HA-g-M2005 compared to those obtained when the reaction was performed in water. However, the reaction systematically led to covalent cross-linking in the case of the HA, with the highest starting molar masses resulting in a very different rheological behaviour and with higher gel strength retaining thermo-responsive behaviour but being only poorly soluble in water.
Keywords: Jeffamine® M2005; hyaluronic acid; hydrogel; thermo-responsive.