Purpose: The effect of flushing at different temperatures on the preparation ability of rotary nickel-titanium files was investigated to provide guideline for clinical application.
Methods: Sixty ProTaper Universal F1 rotary nickel-titanium files were randomly divided into three groups treated by flushing at 6°C, 23°C, and 40°C. Root canal preparation was conducted by step-by-step method on standardized nickel-titanium instrument fracture models. During preparation, the thrust force was set as 10 N, and water was continuously flushed. The motor speed was 350 rpm (rounds per minute), and the torque was 3.0 N cm. When the set torque was reached, the motor automatically rotated in the reverse direction and was pulled out.
Results: Root canal preparation was performed using ProTaper Universal F1 rotary nickel-titanium files treated by flushing. The numbers of rotations before the device was fracture were 429.33 ± 214.68, 821.92 ± 410.43, and 1304.92 ± 297.81, respectively. When each root canal was completed, the numbers of instrument rotations were 272.15 ± 88.30, 188.85 ± 34.36, and 163.41 ± 16.18, respectively. Rank sum test and analysis of variance were performed by IBM SPSS Statistics v21.0 software, and both of them were p < 0.01, indicating that the number of cycles to failure (NCF) and the number of instrument rotations for each root tube were statistically different at the three temperatures.
Conclusions: The self-made resin-simulated curved root canal can replace the real root canal to complete the root canal preparation experiment. The group of nickel-titanium files treated by flushing at 23°C can prepare more root canals and prolong the life of nickel-titanium files than at 6°C. When flushing was done at 40°C, the number of root canals prepared by nickel-titanium files was the highest, and it was not easy to damage the instrument, but lateral perforation occurred easily during root canal preparation.
Keywords: Rotary nickel-titanium files; flushing temperature; resin module; root canal preparation.