The health monitoring of structures is of great interest in order to check components' structural life and monitor damages during operation. Self-monitoring materials can provide both the structural and monitoring functionality in one component and exploit their piezoresistive behavior, namely, the variation of electrical resistivity with an applied mechanical strain. In this work, self-monitoring plies were developed to be inserted into glass-fiber reinforced epoxy-based laminates in order to achieve structural monitoring. Nanocomposite epoxy-based resins were developed employing different contents of high surface area carbon black (CB, 6 wt%) and multiwall carbon nanotubes (MWCNT, 0.75 and 1 wt%), and rheologically and thermomechanically characterized. Self-monitoring plies were manufactured by impregnating glass woven fabrics with the resins, and were laminated with non-sensing plies via a vacuum-bag process to produce sensored laminates. The self-monitoring performance of the laminates was assessed during monotonic and cyclic three-point bending tests, as well as ball drop impact tests. A higher sensitivity was found for the CB-based systems (Gauge Factor 6.1), while MWCNTs (0.55 and 1.04) ensure electrical percolation at lower filler contents, as expected. The systems also showed the capability of being used to predict residual life and damage occurred under impact.
Keywords: glass-fiber-reinforced laminates; polymer matrix composite; self-monitoring.