We investigated a spray drying process for preparing water-soluble salts of high molecular weight chitosan (CH) intended for pharmaceutical excipient applications. CH was derived from chitin of marine lobster origin (Panulirus argus). The effects of organic acid (acetic or lactic acid) and the ratio (difference) of inlet/outlet air temperature (140/90 °C or 160/100 °C) on spray drying were studied. The yield of spray-dried CH salt powders ranged from 50% to 99% in laboratory and industrial-scale processes. The spray-dried dry powder of CH salts consisted of spherical agglomerated particles with an average diameter of 36.2 ± 7.0 µm (CH acetate) and 108.6 ± 11.5 µm (CH lactate). After dispersing the spray-dried CH salt powder samples in purified water, the mean particle sizes obtained for the CH acetate salts were 31.4 nm (batch A001), 33.0 nm (A002) and 44.2 nm (A003), and for the CH lactate salts 100.8 nm (batch L001), 103.2 nm (L002) and 121.8 nm (L003). The optimum process conditions for spray drying were found: an inlet air temperature of 160 ± 5 °C, an outlet temperature of 100 ± 5 °C and an atomizer disk rotational speed of 18,200 min-1. The X-ray powder diffraction (XRPD) and differential scanning calorimetry (DSC) results confirmed the amorphous state of the CH salts. The 1H nuclear magnetic resonance (NMR) and Fourier transform infrared (FT-IR) spectra of CH acetate and lactate salts verified that the spray drying process does not affect the polymer backbone. In conclusion, both laboratory and industrial-scale spray drying methods for preparing water-soluble acid salts of CH are reproducible, and the physicochemical properties of the corresponding CH acid salts are uniform.
Keywords: chitosan salt; organic acid; pharmaceutical excipient; physical material properties; process parameters; scale up; spray drying.