The properties of hybrid silica xerogels obtained by the sol-gel method are highly dependent on the precursor and the synthesis conditions. This study examines the influence of organic substituents of the precursor on the sol-gel process and determines the structure of the final materials in xerogels containing tetraethyl orthosilicate (TEOS) and alkyltriethoxysilane or chloroalkyltriethoxysilane at different molar percentages (RTEOS and ClRTEOS, R = methyl [M], ethyl [E], or propyl [P]). The intermolecular forces exerted by the organic moiety and the chlorine atom of the precursors were elucidated by comparing the sol-gel process between alkyl and chloroalkyl series. The microstructure of the resulting xerogels was explored in a structural theoretical study using Fourier transformed infrared spectroscopy and deconvolution methods, revealing the distribution of (SiO)4 and (SiO)6 rings in the silicon matrix of the hybrid xerogels. The results demonstrate that the alkyl chain and the chlorine atom of the precursor in these materials determines their inductive and steric effects on the sol-gel process and, therefore, their gelation times. Furthermore, the distribution of (SiO)4 and (SiO)6 rings was found to be consistent with the data from the X-ray diffraction spectra, which confirm that the local periodicity associated with four-fold rings increases with higher percentage of precursor. Both the sol-gel process and the ordered domains formed determine the final structure of these hybrid materials and, therefore, their properties and potential applications.
Keywords: (SiO)x structures; FTIR; ORMOSILs; chloroalkyltriethoxysilanes; hybrid materials; inductive effect; xerogels.