From birch wood, it is possible to obtain both acetic acid and 2-furaldehyde as valuable value-added products. The main objective of this study was to develop a new wasteless technology for obtaining 2-furaldehyde, acetic acid, and lignocellulose (LC) residue usable as feedstock in further processing such as thermomechanical (TMP), alkaline peroxide mechanical (APMP), and sulfate pulping processes. To achieve this objective several screening tests were performed, and a further experimental plan was developed using DesignExpert11. Process yields were analyzed both in terms of total yield and at individual time increments. In addition, the obtained LC residue was also characterized. A unique bench-scale reactor system was used to obtain an LC material without pentoses and with maximum preservation of cellulose fiber for further research. Studies on the deacetylation and dehydration of birch wood hemicelluloses of pentose monosaccharides to 2-furaldehyde and acetic acid using orthophosphoric acid as a catalyst were carried out. Results showed that, depending on the used pre-treatment conditions, the 2-furaldehyde yield was from 0.04% to 10.84% oven dry mass (o.d.m.), the acetic acid yield was from 0.51% to 6.50% o.d.m., and the LC residue yield was from 68.13% to 98.07% o.d.m. with minimal content of admixtures. Process optimization using DesignExpert11 revealed that the main pre-treatment process parameters that influenced the yield of 2-furaldehyde in the pre-treatment process were process temperature (53.3%) and process duration (29.8%).
Keywords: 2-furaldehyde; birch wood; lignocellulose; monosaccharides; pre-treatment.