Metal injection molding (MIM) is a near net shape manufacturing method that allows for the production of components of small to moderate size and complex shape. MIM is a cost-effective and flexible manufacturing technique that provides a large innovative potential over existing methods for the industry of implantable devices. Commercially pure titanium (CP-Ti) samples were machined to the same shape as a composite feedstock with titanium and polyoxymethylene, and these metals were injected, debinded and sintered to assess comparative biological properties. Moreover, we treated MIM-Ti parts with BIOCOAT®, BIODIZE® and BIOCER®, three different anodic oxidation techniques that treat titanium using acid, alkaline and anion enriched electrolytes, respectively. Cytocompatibility as well as morphological and chemical features of surfaces was comparatively assessed on each sample, and the results revealed that MIM-Ti compared to CP-Ti demonstrated a specific surface topography with a higher roughness. MIM-Ti and BIOCER® samples significantly enhanced cell proliferation, cell adhesion and cell differentiation compared to CP-Ti. Interestingly, in the anodization post-treatment established in this study, we demonstrated the ability to improve osseointegration through anionic modification treatment. The excellent biological response we observed with MIM parts using the injection molding process represents a promising manufacturing method for the future implantable devices in direct contact with bones.
Keywords: Anodic oxidation; Biocompatibility; Implant; Metal injection molding; Titanium.
Copyright © 2012 Elsevier B.V. All rights reserved.