Epitaxial low temperature grown GaAs (LT-GaAs) on silicon (LT-GaAs/Si) has the potential for terahertz (THz) photoconductive antenna applications. However, crystalline, optical and electrical properties of heteroepitaxial grown LT-GaAs/Si can be very different from those grown on semi-insulating GaAs substrates ('reference'). In this study, we investigate optical properties of an epitaxial grown LT-GaAs/Si sample, compared to a reference grown under the same substrate temperature, and with the same layer thickness. Anti-phase domains and some crystal misorientation are present in the LT-GaAs/Si. From coherent phonon spectroscopy, the intrinsic carrier densities are estimated to be 1015 cm-3for either sample. Strong plasmon damping is also observed. Carrier dynamics, measured by time-resolved THz spectroscopy at high excitation fluence, reveals markedly different responses between samples. Below saturation, both samples exhibit the desired fast response. Under optical fluences ⩾54μJ cm-2, the reference LT-GaAs layer shows saturation of electron trapping states leading to non-exponential behavior, but the LT-GaAs/Si maintains a double exponential decay. The difference is attributed to the formation of As-As and Ga-Ga bonds during the heteroepitaxial growth of LT-GaAs/Si, effectively leading to a much lower density of As-related electron traps.
Keywords: GaAs; coherent phonon; heteroepitaxy; low temperature growth; terahertz.
© 2021 IOP Publishing Ltd.