This work investigated the tensile characteristics of plain C-Mn steel with an ultrafine grained ferrite/cementite (UGF/C) microstructure and coarse-grained ferrite/pearlite (CGF/P) microstructure. The tensile tests were performed at temperatures between 77 K and 323 K. The lower yield and the ultimate tensile strengths were significantly increased when the microstructure was changed from the CGF/P to the UGF/C microstructures, but the total elongation and the uniform elongation decreased. A microstructural change from the CGF/P microstructure to the UGF/C microstructure had an influence on the athermal component of the lower yield and the ultimate tensile strengths but not on the thermal component. The UGF/C microstructure with a higher carbon content provided a higher strength without losing ductility because cementite particles restrained necking.
Keywords: ductility; grain size; plain C–Mn steel; strength; tensile property.