Additive manufacturing of polymers via material extrusion and its future applications are gaining interest. Supporting the evolution from prototype to serial applications, additional testing conditions are needed. The additively manufactured and anisotropic polymers often show a weak point in the interlayer contact area in the manufacturing direction. Different process parameters, such as layer height, play a key role for generating the interlayer contact area. Since the manufacturing productivity depends on the layer height as well, a special focus is placed on this process parameter. A small layer height has the objective of achieving better material performance, whereas a larger layer height is characterized by better economy. Therefore, the capability- and economy-oriented variation was investigated for strain rates between 2.5 and 250 s-1 under tensile and shear load conditions. The test series with dynamic loadings were designed monitoring future applications. The interlayer tensile tests were performed with a special specimen geometry, which enables a correction of the force measurement. By using a small specimen geometry with a force measurement directly on the specimen, the influence of travelling stress waves, which occur due to the impact at high strain rates, is reduced. The interlayer tensile tests indicate a strain rate dependency of additively manufactured polymers. The capability-oriented variation achieves a higher ultimate tensile and shear strength compared to the economy-oriented variation. The external and internal quality assessment indicates an increasing primary surface profile and void volume content for increasing the layer height.
Keywords: additive manufacturing; high-speed testing; interlayer tensile strength; material extrusion.