Bainitic steels were the focus of this study. These steels have the potential to obtain a good combination of strength, ductility, and edge stretchability, which is a very desirable characteristic in the automotive industry. Cu precipitation potential was investigated during prolonged isothermal bainitization treatment. Precipitation strengthening and ductility were measured using a tensile test, and edge stretchability was measured using a hole expansion test. The microstructure was characterized by high-resolution scanning electron microscopy and an electron backscattered diffraction. Lower bainite was obtained by austenitization treatment and subsequent immersion into a salt bath at 400 °C. Cu precipitation occurred after 120 min of holding in the bath and enhanced the yield stress of the Cu-alloyed steel by 120 MPa as compared with a reference steel without Cu. The strengthening did not affect ductility and decreased the edge stretchability by 10%. Steels with different Mn contents were examined. It was found that the enhancement of Mn content from 1 to 2 wt.% did not boost Cu strengthening ability. This result showed that the presence of Mn did not cause an Mn-Cu precipitation strengthening synergy, observed previously during martensite tempering procedure.
Keywords: bainite; copper precipitation; hole expansion test; manganese.