The research on the diffusion of water in coatings has been a hot topic in many fields, such as chemistry, coating structure and hydrogen bonding. In this paper, DGEBA epoxy coating was used as a sample to explore the diffusion process of 3 wt.% NaCl solution at different temperatures. Two-stage diffusion was established by immersion experiment and MD simulation. The synergistic effect of temperature and water on DGEBA properties was revealed by FTIR method and adsorption-desorption cyclic testing. The results showed that as the temperature increased, the saturation water content in coatings increased. At different temperatures, the diffusion process of water presented two-phase characteristics, and the influence of temperature on the diffusion process was mainly manifested in the cross-linking density at higher locations. Based on the variation law of swelling coefficient in per unit time (24 h), the conditions for water-coating interaction and formation of water clusters in this paper were proposed. The synergistic effect of water and temperature on DGEBA properties was reflected in two aspects: at lower temperature (20 °C), water would only change the physical structure of the coatings, while the water broke the DGEBA chains at higher temperature (60 °C).
Keywords: Temperature; adsorption-desorption cycles; epoxy coatings; swelling coefficient; two-stage diffusion.
© 2021 The Author(s). Published by Informa UK Limited, trading as Taylor & Francis Group.