In recent years, recycled aggregate concrete (RAC) has become a research hotspot in the field of urban construction because of its resource utilization of construction waste. However, compared with original concrete, its strength is still low, which requires additional nano-SiO2 (NS) and fiber. In order to study the mechanism of strength improvement of RAC, this paper takes NS and polyvinyl alcohol (PVA) fiber as variable parameters; uniaxial and triaxial compression tests were carried out on RAC with PVA fiber and NS, and the mechanical properties of RAC were investigated The result shows that within the range of 3% NS content, an increase in the NS substitution rate causes the mechanical properties of RAC to improve significantly. The compressive strength of RAC increases again after adding PVA fiber; through a SEM (scanning electron microscopy) analysis of the specimen, it was found that the NS filled the micro-pores and micro-cracks in the RAC, and the PVA fiber changed the contact range between recycled aggregate and mortar, so the microstructure of the material was more compact. The mechanism of RAC strength improvement is explained in the microcosmic view.
Keywords: SEM; conventional triaxial compression; nano-SiO2; polyvinyl alcohol (PVA) fiber; recycled concrete; uniaxial compression.