In this study, the Fe-8Cr-3V-2Mo-2W tool steel powder was deposited on the SCM420 substrate through the directed energy deposition (DED) process. This study focuses on the mechanical properties of the deposited Fe-8Cr-3V-2Mo-2W and the effect of heat treatment on it. The changes in the microstructural characteristics of the deposited region due to heat treatment after deposition were observed. The influence of heat treatment on the mechanical properties was then analyzed accordingly and hence, the hardness, wear, impact and tensile tests were conducted on the deposited material. These properties were compared with those of the commercial tool steel powder M2-deposited material and the carburized specimen. In the deposited Fe-8Cr-3V-2Mo-2W layer, an increased martensite phase fraction was obtained through post-heat treatment and the amount of precipitated carbides was also increased. This increased the hardness from 48 to 62 HRc after heat treatment and the wear resistance was significantly improved as well. The amount of impact energy absorbed decreased from 11 J before heat treatment to 6 J after heat treatment, but the tensile strength significantly increased from 607 to 922 MPa. When compared with the M2-deposited surface, the Fe-8Cr-3V-2Mo-2W deposits had 3% lower surface hardness and 76% lower fracture toughness but exhibited 56% higher tensile strength. When compared with the carburized SCM420, the Fe-8Cr-3V-2Mo-2W deposits exhibited 3% higher surface hardness and wear resistance, 90% lower fracture toughness and 5% higher tensile strength. This study shows that surface hardening through DED can exhibit similar or superior mechanical properties when compared to carburizing.
Keywords: carburization; directed energy deposition (DED); heat treatment; mechanical properties; tool steel.