The influence of chemically converted GO (graphene oxide) functionalized with APTES (3-aminopropyl-triethoxysilane) and unfunctionalized GO, dispersed in ethanolic solution of TEOS (tetraethyl orthosilicate), on the performances of the mortar samples, such as capillary water absorption and compressive strength was evaluated. The effect of the GO based nanomaterials (GO and GO functionalized with APTES) on the mortar microstructure was investigated by Fourier transform infrared spectroscopy (FT-IR), X-ray diffraction (XRD), Raman spectroscopy and scanning electron microscopy (SEM). The multifunctionality of the mortar brushed with GO based nanomaterials consolidation suspension was proved by the results (i) of the mechanical tests which show an improvement of the compressive strength and (ii) the capillary water absorption results which indicate the decreasing of the water penetration speed. For the mortar samples brushed with GO consolidation suspension, an increase value for the compressive strength of approximately twice compared to the untreated control samples and a decreased value for the capillary absorption water coefficient with one order of magnitude in comparison with the untreated control samples were obtained.