Ultrathin transparent conductive oxides (TCOs) are emerging candidates for next-generation transparent electronics. Indium oxide (In2O3) incorporated with post-transition-metal ions (e.g., Sn) has been widely studied due to their excellent optical transparency and electrical conductivity. However, their electron transport properties are deteriorated at the ultrathin two-dimensional (2D) morphology compared to that of intrinsic In2O3. Here, we explore the domain of transition-metal dopants in ultrathin In2O3 with the thicknesses down to the single-unit-cell limit, which is realized in a large area using a low-temperature liquid metal printing technique. Zn dopant is selected as a representative to incorporate into the In2O3 rhombohedral crystal framework, which results in the gradual transition of the host to quasimetallic. While the optical transmittance is maintained above 98%, an electron field-effect mobility of up to 87 cm2 V-1 s-1 and a considerable sub-kΩ-1 cm-1 ranged electrical conductivity are achieved when the Zn doping level is optimized, which are in a combination significantly improved compared to those of reported ultrathin TCOs. This work presents various opportunities for developing high-performance flexible transparent electronics based on emerging ultrathin TCO candidates.
Keywords: liquid metal printing; nonlayered; optical transmittance; transparent conductive oxide; transparent electronics.