Lowering the energy barrier of water dissociation is critical to achieving highly efficient hydrogen evolution in alkaline conditions. Herein, we reported mesoporous RhRu nanosponges with enhanced water dissociation behavior as a new class of high-performance electrocatalysts for alkaline hydrogen evolution reaction (HER). The obtained nanosponges have a binary alloy structure (fcc) and a highly porous structure with high surface area. Our RhRu catalyst displayed an outstanding HER activity with an overpotential of 25 mV at 10 mA cm-2 and a Tafel slope of 47.5 mV dec-1 in 1.0 M KOH, which significantly outperformed that of commercial Pt/C catalyst and was even comparable to the classic Pt/metal (hydro)oxide catalysts. Density functional theory (DFT) calculations disclosed that charge redistribution on the RhRu alloy surface enabled tuning of the Ru d-band center and then promoted the adsorption and dissociation of water molecules. Based on the experimental results and theoretical modeling, a bifunctional mechanism contributed to the remarkable alkaline HER activity on the RhRu catalyst surface.
Keywords: RhRu alloy; bifunctional mechanism; hydrogen evolution reaction; mesoporous metal; water dissociation.