The aim of this study is to develop a novel decellularization method using aqueous extract of soap nut pericarp (SPE) and its evaluation using hematoxylin-eosin staining, scanning electron microscopy, diamidino-2-phenylindol (DAPI) staining, mechanical testing, sodium dodecyl sulfate polyacrylamide gel electrophoresis and DNA quantification. The presently available decellularization agent raises some concerns due to the potential for presence of residual cytotoxic agents in the extracellular matrix. Histological analysis of hematoxylin and eosin and masson's trichrome stained processed aortic samples shows complete decellularization with preservation of extracellular matrix microarchitecture at 120 h. Further, staining of tissue samples with DAPI demonstrates complete removal of DNA fragments. Quantitative evaluation of DNA in the decellularized aorta tissues demonstrated a significant (P < 0.01) decrease in DNA content as compared to native tissues. Collagen quantification assay indicate no significant (P> 0.05) difference in its content between native and decellularized caprine aorta. Tensile strength of the decellularized scaffolds decreased non-significantly (P > 0.05) when compared to native tissues. There was no significant (P > 0.05) difference in young's modulus of elasticity, stiffness and stretch ratio between native aortic tissues and decellularized aortic scaffolds. Histological and scanning electron microscopic examination of in vitro cultured scaffold demonstrated the cell viability and proliferation of primary chicken embryo fibroblasts. SPE treatment is thus capable of producing cytocompatible decellularized caprine aorta scaffold with preservation of extracellular matrix architecture for vascular tissue engineering and could be applied widely as one of the decellularization agent.
Keywords: Caprine aorta; DAPI staining; Decellularization; Histology; Mechanical testing; SEM.
Copyright © 2020 Elsevier Ltd. All rights reserved.