Tunicate is a kind of marine animal, and its outer sheath consists of almost pure Iβ crystalline cellulose. Due to its high aspect ratio, tunicate cellulose has excellent physical properties. It draws extensive attention in the construction of robust functional materials. However, there is little research on its biological activity. In this study, cellulose enzymatic hydrolysis was conducted on tunicate cellulose. During the hydrolysis, the crystalline behaviors, i.e., crystallinity index (CrI), crystalline size and degree of polymerization (DP), were analyzed on the tunicate cellulose. As comparisons, similar hydrolyses were performed on cellulose samples with relatively low CrI, namely α-cellulose and amorphous cellulose. The results showed that the CrI of tunicate cellulose and α-cellulose was 93.9% and 70.9%, respectively; and after 96 h of hydrolysis, the crystallinity, crystalline size and DP remained constant on the tunicate cellulose, and the cellulose conversion rate was below 7.8%. While the crystalline structure of α-cellulose was significantly damaged and the cellulose conversion rate exceeded 83.8% at the end of 72 h hydrolysis, the amorphous cellulose was completely converted to glucose after 7 h hydrolysis, and the DP decreased about 27.9%. In addition, tunicate cellulose has high anti-mold abilities, owing to its highly crystalized Iβ lattice. It can be concluded that tunicate cellulose has significant resistance to enzymatic hydrolysis and could be potentially applied as anti-biodegradation materials.
Keywords: crystalline; enzymatic hydrolysis; tunicate cellulose.