Ti-5Al-4Sn-2Zr-1Mo-0.25Si-1Nb (TA32) titanium alloy is a kind of near α high temperature titanium alloy with great application prospects in aero-engine afterburners and cruise missiles. However, there are still few studies on the microstructure and mechanical properties of TA32 specimens produced by selective laser melting (SLM) technology. In this study, TA32 specimens with high strength (tensile strength of 1267 MPa) and moderate ductility (elongation after fracture of 8%) were obtained by selective laser melting. The effect of laser power on the microstructure and mechanical behavior was studied and the results demonstrated that the average grain size increases with increasing laser power from 200 W to 400 W. Micro-zone composition analysis was carried out by energy dispersion spectrum (EDS), showing that the Al concentration inner grains is higher than that near grain boundaries. Fracture analysis results demonstrated that the fracture mode of SLM TA32 specimens was cleavage fracture. The tensile strength of the specimens built with a laser power of 250 W at 500 °C, 550 °C and 600 °C was measured as 869 MPa, 819 MPa and 712 MPa, respectively.
Keywords: TA32 titanium alloy; mechanical properties; micro-zone composition analysis; microstructure; selective laser melting.