One-dimensional zinc-manganate oxide hollow nanostructures with enhanced supercapacitor performance

Hongge Yun; Xuejiao Zhou; Heran Zhu; Mingyi Zhang

doi:10.1016/j.jcis.2020.11.060

One-dimensional zinc-manganate oxide hollow nanostructures with enhanced supercapacitor performance

J Colloid Interface Sci. 2021 Mar:585:138-147. doi: 10.1016/j.jcis.2020.11.060. Epub 2020 Nov 19.

Authors

Hongge Yun¹, Xuejiao Zhou², Heran Zhu¹, Mingyi Zhang³

Affiliations

¹ Key Laboratory for Photonic and Electronic Bandgap Materials, Ministry of Education, School of Physics and Electronic Engineering, Harbin Normal University, Harbin 150025, People's Republic of China.
² Key Laboratory for Photonic and Electronic Bandgap Materials, Ministry of Education, School of Physics and Electronic Engineering, Harbin Normal University, Harbin 150025, People's Republic of China. Electronic address: zhouxj@hrbnu.edu.cn.
³ Key Laboratory for Photonic and Electronic Bandgap Materials, Ministry of Education, School of Physics and Electronic Engineering, Harbin Normal University, Harbin 150025, People's Republic of China; School of Materials Science and Engineering, Zhengzhou University, Zhengzhou 45001, People's Republic of China. Electronic address: zhangmingyi@hrbnu.edu.cn.

PMID: 33279696
DOI: 10.1016/j.jcis.2020.11.060

Abstract

Hollow electrode materials with structural advantages of large contact interface and sufficient cavity structures are significant for electrochemical energy storage. Herein, ultra-long one-dimensional zinc-manganese oxide (ZnMn₂O₄) hollow nanofibers were successfully prepared by electrospinning at an appropriate temperature (500 °C). The optimal electrode of ZnMn₂O₄ exhibited a larger specific capacitance (1026 F g^-1) as compared to ZnMn₂O₄ powder (125 F g^-1) at a current density of 2 A g^-1 in three-electrode configuration. Moreover, the optimal electrode of the ZnMn₂O₄ hollow nanofibers also possessed long-term cycling stability with a slight upward capacitance (100.8%) after 5000 cycles. Their higher specific capacitance and the outstanding cycle stability may be attributed to the unique 1D hollow nanostructure, which enhanced the charge transfer and improved the diffusion of the electrolyte ions at the surface. Thus, this work designed a high-performance electrode with unique hollow nanostructure that can be applied to the field of energy storage.

Keywords: Electrospinning; Hollow nanofibers; Supercapacitors; ZnMn(2)O(4).