This paper presents the results of experimental research and numerical calculations regarding the static strength and fatigue life of hybrid joints. In the experiments, specimens built as single-lap adhesive-mechanical joints (hybrid joints) were tested. In a two-stage process of the failure of the hybrid joints, the adhesive joint was damaged first. Therefore, it was assumed that the assembly of fasteners closer to the edge of the overlap (beyond the ranges recommended for mechanical joints) limits the negative impact of the peeling phenomenon on the strength and performance properties of hybrid joints. The specimens used in the experiments were prepared from composite elements (i.e., carbon fiber-reinforced polymer (CFRP)), as well as from the aluminum alloy 2024T4. Because the detection of fatigue damage in composite materials is a complex problem, computed tomography was used to evaluate the degradation of the composite material. Experimental and numerical comparative analyses of the static strength and fatigue life of hybrid joints with adhesive and mechanical joints confirmed the assumptions made.
Keywords: fastener; fatigue life; hybrid joint; static strength.