The direct growth of vertically oriented graphene (VG) on low-priced, easily accessible soda-lime glass can propel its applications in transparent electrodes and energy-relevant areas. However, graphene deposited at low temperature (∼600 °C) on the catalysis-free insulating substrates usually presents high defect density, poor crystalline quality, and unsatisfactory electrical conductivity. To tackle this issue, we select high borosilicate glass as the growth substrate (softening point ∼850 °C), which can resist higher growth temperature and thus afford higher graphene crystalline quality, by using a radio-frequency plasma-enhanced chemical vapor deposition (rf-PECVD) route. A nitrogen doping strategy is also combined to tailor the carrier concentration through a methane/acetonitrile-precursor-based synthetic strategy. The sheet resistance of as-grown nitrogen-doped (N-doped) VG films on high borosilicate glass can thus be lowered down to ∼2.3 kΩ·sq-1 at a transmittance of 88%, less than half of the methane-precursor-based PECVD product. Significantly, this synthetic route allows the achievement of 30-inch-scale uniform N-doped graphene glass, thus promoting its applications as excellent electrodes in high-performance switchable windows. Additionally, such N-doped VG films were also employed as efficient electrocatalysts for electrocatalytic hydrogen evolution reaction.
Keywords: hydrogen evolution reaction; nitrogen-doping; plasma-enhanced chemical vapor deposition; switchable window; vertically oriented graphene.