Fiber-reinforcement is a well-established technique to enhance the tensile properties of polymer composites, which is achieved via changing the reinforcing material concentration and orientation. However, the conventional method can be costly and may lead to poor compatibility issues. To overcome these challenges, we demonstrate the use of micro-/nanolayer (MNL) extrusion technology to tune the mechanical properties of polypropylene (PP)/polyethylene terephthalate (PET) fibrillar blends. PET nanofibers-in-PP microfiber composites, with 3, 7, and 15 wt.% PET, are first prepared using a spunbond system to induce high aspect-ratio PET nanofibers. The PP/PET fibers are then reprocessed in an MNL extrusion system and subjected to shear and extensional flow fields in the channels of the uniquely designed layer multipliers. Increasing the mass flow rate and number of multipliers is shown to orient the PET nanofibers along the machine direction (MD), as confirmed via scanning electron microscopy. Tensile tests reveal that up to a 45% and 46% enhancement in elastic modulus and yield strength are achieved owing to the highly aligned PET nanofibers along the MD under strongest processing conditions. Overall, the range of tensile properties obtained using MNL extrusion implies that the properties of fiber-reinforced composites can be further tuned by employing this processing technique.
Keywords: deformation ratio; micro-/nanolayered extrusion; nanofiber alignment; nanofibrillation; shear stress; tensile properties.