The continuous increase in anthropogenic activities resulting in an increase in boron concentration in the environment is becoming a serious threat to public health and the ecosystem. In this regard, a hybrid polyvinylidene fluoride (PVDF)-polyvinyl pyrrolidone (PVP) hollow fiber was synthesized with hydrophilic nano-titanium oxide (TiO2) at varied loadings of 0, 0.5, 1.0, 1.5, and 2.0 wt% using the phase inversion technique. The resultant membranes were characterized in terms of Scanning Electron Microscopy (SEM), Energy Dispersive X-ray Spectroscopy (EDX), contact angle, porosity, and zeta potential. The permeability flux was assessed using both pure water and leachate; also, rejection performance was evaluated based on boron removal from the leachate. The results revealed that the membrane with 1.0 wt% loading had the highest flux alongside an upturn in boron rejection percentage of 223 L/m2·h and 94.39%, respectively. In addition, the lowest contact angle of 50.01° was recorded with 1.0 wt% TiO2 loading, and this implies that it is the most hydrophilic. Throughout the experiment cycles, the fiber with 1.0 wt% TiO2 loading demonstrated a high flux recovery varying between 92.82% and 76.26% after 9 h filtration time. The physicochemical analysis of the permeate revealed that the boron concentration was significantly reduced to 0.43 mg/L, which is far lower than the discharge limit of 1.0 mg/L.
Keywords: antifouling; boron removal; flux; hollow fiber; hydrophilicity; nano-TiO2.