Objectives: The purpose of this study was to evaluate the effect of bacterial cellulose nanocrystals (BCNCs) on the mechanical properties of resin-modified glass ionomer cements (RMGICs) including compressive strength (CS), diametral tensile strength (DTS), and modulus of elasticity (E).
Materials and methods: BCNCs were incorporated into RMGIC at various concentrations (0.3, 0.5, and 1 wt%). Unmodified RMGIC was used as the control group. The specimens were stored in distilled water at 37°C for 24 hours. CS and DTS, as well as modulus of elasticity, were evaluated using a universal testing machine. The nanostructure of BCNCs was observed via field emission scanning electron microscopy.
Statistical analysis: One-way analysis of variance and post-hoc Tukey tests were used for data analysis. Level of significance was at p < 0.05.
Results: The addition of BCNCs to RMGIC led to an increase in all of the tested mechanical properties compared with the control group, with a significant increase observed for 1 wt% BCNC. CS and DTS improved up to 23%, and modulus of elasticity increased by 44%.
Conclusions: The addition of BCNCs to the RMGIC improved the mechanical properties, including CS, elastic modulus, and DTS. Thus, the newly developed RMGICs with BCNCs might represent an ideal and promising novel dental material in restorative dentistry.
European Journal of Dentistry. This is an open access article published by Thieme under the terms of the Creative Commons Attribution-NonDerivative-NonCommercial-License, permitting copying and reproduction so long as the original work is given appropriate credit. Contents may not be used for commercial purposes, or adapted, remixed, transformed or built upon. (https://creativecommons.org/licenses/by-nc-nd/4.0/).