As a representative of the third generation of advanced high strength steel, the quenching and partitioning steel has excellent potential in automobile manufacturing. The characterization and analysis of the mechanical properties and microstructure of the quenching and partitioning steel during deformation is an effective way to explore the microstructure evolution and transformation-induced plasticity effects of complex phase steels. The relationship between the microstructure morphology and mechanical properties of a 1180 MPa-grade quenching and partitioning steel was investigated through interrupted uniaxial tensile tests plus quasi-situ electron backscatter diffraction measurements. A mixture of ferrite, martensite, and retained austenite was observed in the microstructure. It was found that the volume fraction of global retained austenite decreased linearly with the increase of displacement (0 mm-1.05 mm). The evolution of the retained austenite with typical crystal direction ranges with deformation was characterized. Results show that the orientation (111) and (311) account for the highest proportion of retained austenite grains in the undeformed sample and the mechanical stability of the (311) retained austenite grains is the best. Moreover, the retained austenite grains rotated significantly in the early stage of the specimen deformation process (around yielding), and the work hardening of the specimen was weak at this stage, simultaneously.
Keywords: anisotropy; mechanical properties; microstructure; quasi-situ electron backscatter diffraction; quenching and partitioning steel; retained austenite.