The development of both light and strong wood-derived materials is an interesting research area, particularly in terms of usability in, e.g., furniture constructions. Honeycomb panels being current industry standard are relatively thick (32 mm and 40 mm), thus their attractiveness in designing furniture is limited. In a few studies, it has been shown that honeycomb panels with paper cores are characterized by unsatisfactory mechanical properties, especially when the composite thickness is less than 20 mm. From the literature, it is also evident that mechanical properties might be improved by introducing auxetic features into the core structure. Even though it is a concept with great potential, there are a few studies dealing with honeycomb panels with auxetic cores made of paper. Furthermore, there is no research on the corner joints made from such material. For this reason, the aim of the study was to test the bending behavior of the corner adhesive joints made of honeycomb panels with double arrow-shaped auxetic cores. Within the research, the core cell was adopted based on literature and preliminary studies, paper auxetic cores were produced by the use of the designed and 3d printed device, and joints stiffness and strength were calculated analytically based on the experiment results. Evaluated corner joints stiffness, both in compression and tension test, is greater for samples made of panels with designed auxetic cores. Surprisingly, in the analyzed range of elasticity, it was statistically proved that the values of joint stiffness coefficient K did not vary significantly between compared joints pairs.
Keywords: auxetic; corner; honeycomb; joints; stiffness; strength.