Single crystals of SmAl3(BO3)4 were synthesized by the group growth on seeds method. The crystal structure was solved using a single-crystal experiment and the purity of the bulk material was proved by the Rietveld method. This borate crystallizes in the monoclinic C2/c space group with unit-cell parameters a = 7.2386 (3), b = 9.3412 (5), c = 11.1013 (4) Å and β = 103.2240 (10)°. IR and Raman spectroscopic analyses confirmed the monoclinic structure of SmAl3(BO3)4. Under 532.1 nm excitation, luminescence spectra exhibit bands assignable to the transitions from 4G5/2 to 6H5/2, 6H7/2, 6H9/2 and 6H11/2. The similarity of the luminescence spectra of the trigonal and monoclinic polymorphs is explained by the minor role of Sm-O bond distortion and the primary role of rotational distortion of SmO6 octahedra. The smaller covalency of the Sm-O bond in alumoborates is deduced in comparison with galloborates. Calorimetric measurements did not reveal high-temperature structural phase transitions up to a temperature of 720 K.
Keywords: IR spectroscopy; Raman spectroscopy; X-ray diffraction; crystal structure; luminescence; monoclinic structure.