Yellow mealworms (Tenebrio molitor larvae) are capable of biodegrading polystyrene (PS) and low-density polyethylene (LDPE). This study tested biodegradation of one expanded PS (EPS) with a weight-average molecular weight (Mw) 256.4 kDa and two LDPE foams with respective Mw of 130.6 kDa (PE-1) and 288.7 kDa (PE-2) in T. monitor larvae obtained in Beijing, China. The larvae consumed EPS and both LDPEs over a 60 day. Fourier transform infrared spectroscopy and thermogravimetric analyses of frass confirmed the formation of new oxygen-containing functional groups, as well as a change in physical property and chemical modification, indicating that biodegradation of EPS and LDPE occurred. Gel permeation chromatography analysis confirmed broad depolymerization of EPS and PE-1 (i.e., a decrease in both Mw and a number-average molecular weight (Mn)) but revealed limited extent depolymerization of PE-2 (i.e., increase in Mn and decrease in Mw). For all materials, the size-average molecular weight (Mz) was decreased. Biodegradation and oxidation of EPS and LDPE were confirmed using FTIR and TGA analysis. Depression of gut microbes by the antibiotic gentamicin resulted in significant inhibition of EPS depolymerization but did not stop LDPE depolymerization, resulting in the increase in Mn and revealing that PS biodegradation was gut microbe-dependent but LDPE biodegradation was less dependent or independent of gut microbes. Gut microbial community analysis indicated that, as expected, under different dietary conditions, the intestinal flora significantly shifted to communities associated with biodegradation of EPS and LDPE. The results indicated the complexity and limitation of biodegradation of plastics in plastics-eating T. molitor larvae.
Keywords: Biodegradation; Expanded polystyrene; Low density polyethylene; Mealworm; Microbiome; Plastic.
Copyright © 2020. Published by Elsevier Ltd.