To compare the dislodgement resistance and the adhesive pattern of four different endodontic sealers to root dentine walls. Ninety lower premolars were assigned to five groups (n = 18), Group 1: no sealer (control); Group 2: EndoRez (ERZ); Group 3: Sealapex (SPX); Group 4: EndoSeal MTA (ESA) and Group 5: BioRoot RCS (BRS). They were instrumented up to size 30 taper 0.06 and obturated using single cone technique with matched-taper gutta-percha cones and one of the mentioned sealers. Six teeth from each group were then randomly subjected to 100, 1000 and 10,000 thermocycles, respectively. 1 mm slice of mid root region, measuring 6 mm from the apical foramen was prepared and subjected to push-out test under a Universal Testing Machine. Adhesive patterns of sealers were assessed using a stereomicroscope at 20 × magnification and classified using a new system. Statistical analyses were performed using two-way ANOVA, complemented by Tukey HSD and Chi-square tests. ESA and BRS showed significantly higher (p < 0.05) push-out bond strength, followed by SPX, ERZ and lastly the control, but no significant difference was noted between ESA and BRS (p > 0.05) at 100, 1000 and 10,000 thermocycles, respectively. Both ESA and BRS exhibited a significant higher rate (p < 0.05) of Type 3 and Type 4 adhesive patterns as the thermocycles increased. ESA and BRS demonstrated higher bond strength and better adhesive pattern to root dentine wall than SPX and ERZ, especially after artificial ageing.
Keywords: Dislodgement resistance; EndoRez; Mineral trioxide aggregate; Sealapex; Tricalcium silicate.