Sn-based Babbitt alloy was reinforced with alumina nanoparticles to prepare a novel class of nanocomposites. The route of liquid metallurgy in combination with stirring mechanism was chosen to prepare nanocomposites with three different loadings of alumina nanoparticles, i.e., 0.25 wt%, 0.50 wt% and 1.0 wt%. The molten mixture of metallic matrix and nanoparticles was poured over carbon steel substrate for solidification to manufacture a bimetallic material for bearing applications. The underlying aim was to understand the effect of nanoparticle addition on microstructural variation of Sn-based Babbitt alloy as well as bimetallic microstructural interface. The addition of 0.25 wt% and 0.50 wt% alumina nanoparticles significantly affected both the morphology and distribution of Cu6Sn5 hard phase in solid solution, which changed from needle and asterisk shape to spherical morphology. Nanocomposites containing up to 0.50 wt% nanoparticles showed more improvement in tensile strength than the one containing 1.0 wt% nanoparticles, due to nanoparticle-agglomeration and micro-cracks at the interface. The addition of 0.5 wt% nanoparticles significantly improved the wear resistance of Sn-based Babbitt alloy.
Keywords: Babbitt; alumina; mechanical; microstructure; nanocomposite; nanoparticle.