The anthracite granules were coated with iron oxide by a solution combustion synthesis method in a muffle furnace oven. As for iron precursor, an iron-containing precipitate of water treatment plants was used. The influence of four different reducing reagents on surface phase composition and properties of the modified materials was investigated. Obtained samples were investigated using different diffraction and spectroscopic methods. Using the solution combustion synthesis method, anthracite granules formed fine dispersed and crystalline structures of iron oxides on their surface with the iron content up to 40.7 wt%. This had a positive effect on the catalytic capacity of the material for deironing of underground water as well as for the increase in specific surface area. The catalytic properties of the obtained samples and the effectiveness of deferrization of groundwater were investigated. The use of tested materials makes it possible to reduce of catalytic layer height of the filter media from 50 to 20 cm for the filtration rate 12 m/h and enhance the treatment efficiency during the first start-up of filters after regeneration up to 3 times.
Keywords: Anthracite; Deironing sludge; Modified surface; Solution combustion synthesis; Underground water.