The deformation-induced crystallization of an isotactic polypropylene (iPP) sheet containing a β-nucleating agent was evaluated. The phase transformation of the β-modifications was investigated and the crystal morphology was observed at room temperature after stretching at different temperatures. The results showed that the crystallinity increased after solid-state stretching. When the stretching temperature was below the initial crystallization temperature, stretching deformation promoted the orientation of amorphous molecular chains. When the deformation temperature exceeded the crystallization temperature, part of the β-modifications underwent a phase transformation process and was stretched into a shish-kebab structure. However, once the stretching temperature was close to the melting point, the β-modifications melted and recrystallized, and the shish-kebab structure underwent stress relaxation due to poor thermal stability, transforming into α-modifications. It was revealed that the crystal phase transformation mechanism of the β-modifications was based on the orientation of the molecular chains between the adjacent lamellae. In addition, the shish-kebab cylindrite structure played an important role in modifying the tensile and impact properties of the iPP sheet. The tensile and impact strengths increased by as much as 34% and 126%, respectively.
Keywords: cylindrites; phase transformation; solid-state stretching; β-modification iPP sheet.