Lignin displays attractive properties in peripheral nerve applications. Here, aligned polycaprolactone (PCL) fibers with various percentages of lignin nanoparticles were fabricated using the electrospinning method. The morphologies, contact angles, mechanical properties, in vitro degradation, and water uptake of the PCL/lignin fibers were characterized. Cell viability and adhesion of PC12 and human adipose-derived stem cells (hADSCs) were studied employing MTT assay and SEM, respectively. SEM, immunocytochemistry, and Real-Time PCR were utilized to characterize neural differentiation and neurite length of PC12 and hADSCs. To further study on lignin effect on nerve regeneration, in vivo studies were performed. The results indicated that all nanocomposite fibers were smooth and bead-free. With increasing the lignin content, the water contact angle decreased while in vitro degradation, water uptake, and Young's modulus increased compared to the PCL fibers. Cell viability, and differentiation along with neurite length extension were promoted by increasing lignin content. The neural markers expression for differentiated cells were upregulated by the increase of lignin percent. In vivo investigation also demonstrates that sample groups incorporating 15% lignin nanoparticles showed better regeneration among others. Therefore, PCL with 15% of lignin nanoparticles shows great potential to be applied for nerve regeneration.
Keywords: Lignin; Sciatic nerve regeneration; Tissue engineering.
Copyright © 2020. Published by Elsevier B.V.