In this research, the curing degree of an acrylate-based monomer using direct UV-assisted writing technology was characterized by differential photo calorimetry (Photo-DSC) to investigate the curing behavior. Triggered by the UV light, the duo function group monomer 1,6-Hexamethylene diacrylate (HDDA), photoinitiator 1173 and photoinhibitor exhibit a fast curing process. The exothermal photopolymerization reaction was performed in the isothermal mode in order to evaluate the different thermal effects that occurred during the photopolymerization process. The influences of both UV light intensity and exposure time were studied with single-factor analysis. The results obtained by photo-DSC also allow us to perform the kinetic study of the polymerization process: The results show that, for the reaction, the higher the UV intensity, the higher the curing degree together with faster curing speed. At the same time, the effect of the heat released during the exothermic reaction is negligible for the polymerization process. When increasing the exposure time, limited improvement of curing degree was shown, and the distribution is between 65-75%. The reaction enthalpy and related curing degree work as a function of time. The Avrami theory of phase change was introduced to describe the experimental data. The functions of a curing degree with light intensity and exposure time were achieved, respectively.
Keywords: UV curing; additive manufacturing; curing kinetic; photo-DSC; photopolymerization.