As promising fibrous reinforcements in the thick composites manufacturing, 3-dimensional warp interlock fabrics (3DWIFs) are recognised more and more in the industry for their outstanding mechanical properties compared to the 2D laminates. The present work shows the influence of the fabric's architecture on the tensile behaviour of 3DWIFs. Five kinds of 3D fabrics with different interlock structures have been designed according to the main category of binding warp yarn evolution. These five 3DWIFs, containing both binding and stuffer warp yarns and produced with the same warp and weft densities, are experimentally tested via uniaxial tensile tests. The experimental results of the different 3DWIFs have been compared to find the optimal solution based on several mechanical performances. Fabric structures have an impact on tensile properties both in the warp and weft directions. Furthermore, other influential factors, for example, the yarn crimps during the weaving process and the crimp angles of binding warp yarns in 3DWIFs, are investigated and discussed in the paper. The influence of the total crimp angles related to the binding path on the tensile properties of 3DWIFs via the inter yarns friction is summarised.
Keywords: 3D warp interlock fabrics; HMWPE; fabric/textiles; mechanical properties.