Black liquor has caused a tremendous degree of pollution and waste. Exploring the utilization of lignin, which is the major component of black liquor, has become a key factor in dealing with the problem. In this study, lignin derived from black liquor was used as a raw material to prepare carbon materials through different activation methods including KOH, H3PO4, and steam activation. The structure and properties of obtained samples were characterized as well as electrochemical performance when applied on a lithium-oxygen battery. Results of N2 adsorption/desorption showed that all obtained samples possessed high surface area of over 1000 m2/g. XRD, Raman, and XPS also indicated that obtained samples possessed a large defect area and many functional groups. Electrochemical measurements illustrated that all obtained samples exhibited a high discharge capacity over 2.8 mAh/cm2 at 0.02 mA/cm2, while LKAC exhibited the highest discharge capacity of 7.2 mAh/cm2. Cycling tests of all obtained samples indicated a long cycle life of at least 300 cycles. LSAC maintained a 100% retention rate of capacity and stable terminal voltage even after 800th cycle, and its cycling performance was investigated further by XRD and EIS. This study demonstrated excellent performance for lignin-based carbon materials, and provided alternative materials for positive electrode of lithium-oxygen battery.
Keywords: biochar; black liquor; lignin; lithium−oxygen battery.