The grain selection method is widely used in industry to produce Ni-based single crystal superalloys. A Z-form two-dimensional (2D) grain selector was designed to obtain high-quality single crystals. To control grain orientation deviation, one of the most important defects of the single crystal superalloys in casting, Z-form 2D grain selectors with different take-off angle were investigated in this study. The MM247LC superalloy single crystal samples were obtained by the Bridgman method modified by the Z-form grain selectors in this study. The Electron Backscattered Diffraction (EBSD) and the Optical Microscopy (OM) were used to observe and measure the grain selection growth and the microstructural evolution and orientation of the single crystal were also discussed. The results show that a Z-form 2D grain selector with an appropriate take-off angle can significantly reduce the deviation of the grain orientation. A single crystal superalloy with a deviation angle less than 6° can be obtained effectively when the take-off angle was 40°.
Keywords: 2D grain selector; deviation of the grain orientation; directional solidification; single crystal; take-off angle.