Quasi-2D Ruddlesden-Popper halide perovskites with a large exciton binding energy, self-assembled quantum wells, and high quantum yield draw attention for optoelectronic device applications. Thin films of these quasi-2D perovskites consist of a mixture of domains having different dimensionality, allowing energy funneling from lower-dimensional nanosheets (high-bandgap domains) to 3D nanocrystals (low-bandgap domains). High-quality quasi-2D perovskite (PEA)2 (FA)3 Pb4 Br13 films are fabricated by solution engineering. Grazing-incidence wide-angle X-ray scattering measurements are conducted to study the crystal orientation, and transient absorption spectroscopy measurements are conducted to study the charge-carrier dynamics. These data show that highly oriented 2D crystal films have a faster energy transfer from the high-bandgap domains to the low-bandgap domains (<0.5 ps) compared to the randomly oriented films. High-performance light-emitting diodes can be realized with these highly oriented 2D films. Finally, amplified spontaneous emission with a low threshold 4.16 µJ cm-2 is achieved and distributed feedback lasers are also demonstrated. These results show that it is important to control the morphology of the quasi-2D films to achieve efficient energy transfer, which is a critical requirement for light-emitting devices.
Keywords: amplified spontaneous emission; distributed-feedback lasers; energy funneling; light-emitting diodes; quasi-2D perovskites.
© 2020 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.