NiFe2O4 Nanoparticles Synthesized by Dextrin from Corn-Mediated Sol-Gel Combustion Method and Its Polypropylene Nanocomposites Engineered with Reduced Graphene Oxide for the Reduction of Electromagnetic Pollution

Abstract

In this work, nickel ferrite (NiFe₂O₄) nanoparticles were synthesized by dextrin from corn-mediated sol-gel combustion method and were annealed at 600, 800, and 1000 °C. The structural and physical characteristics of prepared nanoparticles were studied in detail. The average crystallite size was 20.6, 34.5, and 68.6 nm for NiFe₂O₄ nanoparticles annealed at 600 °C (NFD@600), 800 °C (NFD@800), and 1000 °C (NFD@1000), respectively. The electromagnetic interference shielding performance of prepared nanocomposites of NiFe₂O₄ nanoparticles (NFD@600 or NFD@800 or NFD@1000) in polypropylene (PP) matrix engineered with reduced graphene oxide (rGO) have been investigated; the results indicated that the prepared nanocomposites consisted of smaller-sized nickel ferrite nanoparticles exhibited excellent electromagnetic interference (EMI) shielding characteristics. The total EMI shielding effectiveness (SE_T) for the prepared nanocomposites have been noticed to be 45.56, 36.43, and 35.71 dB for NFD@600-rGO-PP, NFD@800-rGO-PP, and NFD@1000-rGO-PP nanocomposites, respectively, at the thickness of 2 mm in microwave X-band range (8.2-12.4 GHz). The evaluated values of specific EMI shielding effectiveness (SSE) were 38.81, 32.79, and 31.73 dB·cm³/g, and the absolute EMI shielding effectiveness (SSE/t) values were 388.1, 327.9, and 317.3 dB·cm²/g for NFD@600-rGO-PP, NFD@800-rGO-PP, and NFD@1000-rGO-PP, respectively. The prepared lightweight and flexible sheets can be considered useful nanocomposites against electromagnetic radiation pollution.