A stretchable organic thermoelectric multilayer is achieved by alternately depositing bilayers (BL) of 0.1 wt% polyethylene oxide (PEO) and 0.03 wt% double walled carbon nanotubes (DWNT), dispersed with 0.1 wt% polyacrylic acid (PAA), by the layer-by-layer assembly technique. A 25 BL thin film (~500 nm thick), composed of a PEO/DWNT-PAA sequence, displays electrical conductivity of 19.6 S/cm and a Seebeck coefficient of 60 µV/K, which results in a power factor of 7.1 µW/m·K2. The resultant nanocomposite exhibits a crack-free surface up to 30% strain and retains its thermoelectric performance, decreasing only 10% relative to the unstretched one. Even after 1000 cycles of bending and twisting, the thermoelectric behavior of this nanocomposite is stable. The synergistic combination of the elastomeric mechanical properties (originated from PEO/PAA systems) and thermoelectric behaviors (resulting from a three-dimensional conjugated network of DWNT) opens up the possibility of achieving various applications such as wearable electronics and sensors that require high mechanical compliance.
Keywords: carbon nanomaterials; layer-by-layer assembly; organic multilayers; power factor; stretchable thin films; thermoelectric multilayers.