Objectives: This study evaluated effects of Bioglass 45S5 (BG) and Biosilicate (BS) remineralization on the chemical composition and bond strength of control dentin (CD) and bleached dentin (BD) surfaces.
Methods and materials: Dentin bleaching treatment was performed using the walking bleaching technique with 0.01 g of sodium perborate and 0.5 mL of 3% hydrogen peroxide for 14 days. Remineralization treatment was carried out by rubbing a remineralization solution (0.015 g of BG or BS diluted in 1.35 mL of distilled water) on the etched dentin surface for 30 seconds. Micro-Raman spectroscopy (MRS) was used to quantitatively analyze the mineral matrix ratios of CD and BD (n=5) after remineralization treatment with BG and BS over 15 days of incubation in artificial saliva. The CD and BD discs (n=10) with and without remineralization treatment with BG and BS were restored using a two-step etch-and-rinse adhesive system (Optibond S, Kerr) and five layers of 1-mm-thick composite resin (Filtek Z250, 3M ESPE). The restored dentin discs were sectioned into nine bonded beams with cross-sectional areas of approximately 0.9 mm2 and tested for microtensile bond strength (μTBS). The dentin surface of one fractured beam per tooth was submitted to MRS to characterize the physicochemical composition (n=10) at the interface. The data were analyzed using one-way analysis of variance and the Tukey-Kramer post hoc test (p<0.005).
Results: MRS bioactive analyses revealed that both BG and BS promoted increased mineral matrix ratios in the CD and BD. Significantly higher μTBS values were found after CD treatment with BG (CD: 57 MPa±11; CD-BG: 78 MPa±15) and when BG and BS were applied to the BD (BD: 42 MPa±5; BD-BG: 71 MPa±14; BD-BS: 64 MPa±11) (p<0.005). The MRS analysis of the fractured dentin beam showed that the remineralization treatment significantly increased the dentin relative mineral concentration and promoted the appearance of new interface peaks, indicating a chemical interaction (p<0.005).
Conclusion: Remineralization of BD is an effective therapy to restore damage caused by dentin bleaching and acid conditioning. This approach not only increases dentin mineral compounds but also improves dentin's ability to interact chemically with the adhesive system.