Mesoporous bimetallic Fe/Co was prepared as a Fenton-like catalyst to degrade the tetracycline hydrochlorides (TC). The nanocasting strategy with KIT-6 as a hard template was carried out to synthesize the mesoporous bimetallic catalyst. The mesoporous bimetallic Fe/Co catalyst was characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), nitrogen adsorption-desorption isotherms, and Brunauer-Emmett-Teller (BET) method. The results showed that the catalyst has significant nanofeatures; the surface area, pore size, and particle size were 113.8 m2g-1, 4 nm, and 10 nm, respectively. In addition, the effects of the operating parameters, such as the iron-to-cobalt ratio, pH, H2O2, and initial TC concentrations on its catalytic performance were investigated. The best operating parameters were as follows: iron-to-cobalt ratio = 2:1 to 1:1, pH = 5-9, H2O2: 30 mmol, initial TC less than 30 mg/L. Furthermore, the mesoporous bimetallic Fe/Co showed a good performance for degrading TC, achieving a removal rate of 86% of TC after 3 h under the reaction conditions of H2O2 = 30 mmol, mesoporous bimetallic Fe/Co = 0.6 g/L, TC = 30 mg/L, pH = 7.0, and temperature = 25.5 °C. The mesoporous bimetallic Fe/Co catalyst shows good stability and reusability. This work demonstrated that mesoporous bimetallic Fe/Co has excellent catalytic efficiency, smaller amounts of leached ions, and wider pH range, which enhance its potential applications.