Three-Dimensional Nanoconfinement Supports Verwey Transition in Fe3O4 Nanowire at 10 nm Length Scale

Rupali Rakshit; Azusa N Hattori; Yasuhisa Naitoh; Hisashi Shima; Hiroyuki Akinaga; Hidekazu Tanaka

doi:10.1021/acs.nanolett.9b01222

Three-Dimensional Nanoconfinement Supports Verwey Transition in Fe₃O₄ Nanowire at 10 nm Length Scale

Nano Lett. 2019 Aug 14;19(8):5003-5010. doi: 10.1021/acs.nanolett.9b01222. Epub 2019 Jul 9.

Authors

Rupali Rakshit¹, Azusa N Hattori^{1

2}, Yasuhisa Naitoh³, Hisashi Shima³, Hiroyuki Akinaga³, Hidekazu Tanaka¹

Affiliations

¹ Nanoscience & Nanotechnology Center, The Institute of Scientific and Industrial Research , Osaka University , Mihogaoka 8-1 , Osaka , Ibaraki 567-0047 , Japan.
² JST-PRESTO , Kawaguchi , Saitama 332-0012 , Japan.
³ National Institute of Advanced Industrial Science and Technology , Higashi 1-1-1 , Tsukuba , Ibaraki 305-8562 , Japan.

PMID: 31287324
DOI: 10.1021/acs.nanolett.9b01222

Abstract

Herein, we construct three-dimensional (3D) Fe₃O₄ epitaxial nanowires at a 10 nm length scale on a 3D MgO nanotemplate using an original nanofabrication technique that mainly comprises nanoimprint lithography and inclined thin-film deposition. Despite the high density of inevitable nanoscale defects, the ultrasmall Fe₃O₄ nanowires exhibit a prominent Verwey transition at about 112 K with a maximum relative change in resistance of 9.5, which is 6 times larger than that of the thin-film configuration. Numerous measurements on a large number of Fe₃O₄ nanowires grown concurrently on the same 3D MgO nanotemplate reveal a dramatic difference in their electrical transport property with the presence/absence of the Verwey transition. A comparative study of Fe₃O₄ wires of increasing volume and a thin film reveals that a profound change in the Verwey transition is observed only for wires with a volume on the order of 10 nm³. Moreover, a significant decrease in the sharpness of the resistance jump and the transition temperature of the Verwey response is noticed with an increasing volume of Fe₃O₄. This indicates the potency of the 3D nanofabrication technique in controlling nanoscale defects, which is further reconfirmed through magnetoresistance measurement. A feature of the magnetoresistance curve identifies the antiphase boundaries as a major source of defects. The occurrence of the smallest magnetoresistance in the ultrasmall nanowire with the highest Verwey transition temperature and resistance change ratio proves that 3D isotropic spatial confinement into a length scale comparable to the average spacing between two antiphase boundaries enables the favorable control over nanoscale defects. A simple statistical model satisfactorily illustrates the dependence of electrical transport properties on the volume of Fe₃O₄ from the macroscale down to the nanoscale. Finally, an ultrasmall nanowire with a low defect concentration allows the estimation of the true coherence length of the fundamental quasiparticle, the trimeron, responsible for the Verwey transition.

Keywords: FeO; Verwey transition; intrinsic defect; nanoconfinement; statistical model.