Taper-free InP twinning superlattice (TSL) nanowires with an average twin spacing of ∼13 nm were grown along the zinc-blende close-packed [111] direction using metalorganic vapor phase epitaxy. The mechanical properties and fracture mechanisms of individual InP TSL nanowires in tension were ascertained by means of in situ uniaxial tensile tests in a transmission electron microscope. The elastic modulus, failure strain, and tensile strength along the [111] direction were determined. No evidence of inelastic deformation mechanisms was found before fracture, which took place in a brittle manner along the twin boundary. The experimental results were supported by molecular dynamics simulations of the tensile deformation of the nanowires that also showed that the fracture of twinned nanowires occurred in the absence of inelastic deformation mechanisms by the propagation of a crack from the nanowire surface along the twin boundary.
Keywords: transmission electron microscope mechanical test; InP nanowires; Twinning superlattice; fracture behavior; molecular dynamics.