Objective: The aim of this study was to evaluate the effect of neutralizing agents on the shear bond strength of hydrofluoric (HF)-etched porcelain in nonaging and aging conditions.
Subjects and methods: One hundred and twenty feldspathic porcelain specimens were prepared and divided into six groups to undergo different surface conditioning methods-group 1: control; group 2: HF; group 3: HF + calcium hydroxide; group 4: HF + calcium carbonate; group 5: HF + calcium gluconate; and group 6: HF + ultrasonic. All samples were immersed in 37°C distilled water for 24 h. Half of the samples were thermocycled in water for 5,000 cycles. The shear bond strength test was performed using a universal testing machine at a crosshead speed of 0.5 mm/min. Data were statistically analyzed by two-way ANOVA and Tukey's multiple comparison test at a 95% confidence level. The surface micromorphology and surface elements were analyzed using scanning electron microscope (SEM) and energy-dispersive X-ray spectroscopy (EDX), respectively.
Results: The shear bond strengths of groups 2-6 were significantly higher than the control group in both aging and nonaging conditions (p < 0.05). There were no significant differences among all of the HF-etched porcelain groups (p > 0.05). SEM images of groups 2-6 illustrated similar patterns of irregularity on the specimen surfaces. Elemental analysis of EDX demonstrated identical elements on surfaces of specimens of groups 2-6.
Conclusion: Within the limitations of this study, shear bond strength values between HF-etched porcelain, HF-etching followed by application of neutralizing agents, and HF-etching followed by ultrasonic cleaning were not significantly different in both nonaging and aging conditions.
Dental Investigation Society.