To realize feasible band structure engineering and hence enhanced luminescence efficiency, InGaNBi is an attractive alloy which may be exploited in photonic devices of visible light and mid-infrared. In present study, the structural, electronic properties such as bandgap, spin-orbit splitting energy, and substrate strain of InGaNBi versus In and Bi compositions are studied by using first-principles calculations. The lattice parameters increase almost linearly with increasing In and Bi compositions. By bismuth doping, the quaternary InGaNBi bandgap could cover a wide energy range from 3.273 to 0.651 eV for Bi up to 9.375% and In up to 50%, corresponding to the wavelength range from 0.38-1.9 µm. The calculated spin-orbit splitting energy are about 0.220 eV for 3.125%, 0.360 eV for 6.25%, and 0.600 eV for 9.375% Bi, respectively. We have also shown the strain of InGaNBi on GaN; it indicates that through adjusting In and Bi compositions, InGaNBi can be designed on GaN with an acceptable strain.
Keywords: Electronic; First-principles; InGaNBi; Quaternary; Strain.